A green material ideal for small, fine featured jewelry master patterns for gypsum investment casting applications. This material leaves minimal ash after burnout to produce superior casting quality. Create and produce custom jewelry or other investment castings that capture fine detail with a smooth surface finish.

Applications:

  • Jewelry pattern production
  • Investment casting
  • Prototype pieces
  • Design verification
  • Fitting pieces
  • Resin molds for wax cast and RTV
  • Master patterns for RTV/silicone molds

Technical Specifications

  • Bottle Volume


    1 kg

  • Layer Thickness


    0.030 mm | 0.001 in

  • Vertical Build Speed


    5.3 mm/hr | 0.21 in/hr

  • Liquid Density


    1.10 g/cm3

Cured Part Properties

 

Metric

U.S.

Solid Density
ASTM D792
1.18 g/cm3 0.043 lb/in3
Tensile Strength
ASTM D638
14 MPa 2000 psi
Tensile Modulus
ASTM D638
355 MPa 51.5 ksi
Elongation at Break
ASTM D638
10% 10%
Flexural Modulus
ASTM D790
577 MPa 84 ksi
Flexural Strength
ASTM D790
14 MPa 2030 psi
Tg
DMA, E”
-1 °C 31 °F
CTE >Tg
CTE ASTM E831
185 ppm/°C
169 ppm/°C
102 ppm/°F
94 ppm/°F
Shore Hardness
ASTM D2240
68 D 68 D